EPOXY RESIN RED COATING GEL COAT REPAIR
EPOXY RESIN GRAY COATING GEL COAT REPAIR (MAX GPE GRAY A/B) is a two-component epoxy based resin system designed to provide a broad range of resin application and use. It demonstrates excellent mechanical and physical properties that is suitable for almost all types of epoxy resin applications.
MAX GPE RED A/B is mixed two parts Resin to one part Curing Agent by weight or by volume (2:1). The mixed consistency is very low in viscosity, clear and easily poured or applied in to place resulting in bubble free castings. MAX GPE A/B MEDIUM SET has a 60 minutes gel time that allows adequate working time for casting, coating, bonding and potting or encapsulating applications.
MAX GPE RED A/B performs well as an adhesive for metals, alloys, plastic, wood, stones products, fiberglass, carbon fiber composites and concrete and other substrates that require high tensile shear strength properties. Higher adhesion performance can be achieved after a post cure cycle of 1 hour at 120°C.
MAX GPE RED A/B Coating properties exhibits very high gloss, good color stability, high surface and excellent chemical resistance. Optimized amounts UV inhibitors, anti-oxidants and stabilizers are incorporated with the MAX GPE A/B MEDIUM SET to provide added outdoor durability. An aliphatic polyurethane coating should be applied to further improved resistance to UV degradation.
MAX GPE RED A/B can be used as a protective or decorative coating for metals, alloys, plastic, wood, stones products, fiberglass, carbon fiber composites and concrete and other substrates Higher coating performance can be achieved after a post cure cycle of 1 hour at 120°C.
MAX GPE A/B MEDIUM SET is an excellent choice for composite fabrication using fiberglass, carbon fiber, Aramid, and other hybrid fabrics. Its low viscosity allows fast fabric wet-out resulting in minimal void and laminate porosity. Cured composites fabricated with
MAX GPE A/B MEDIUM SET exhibits exceptional mechanical properties such as impact resistance, compressive and tensile strength. Higher mechanical performance can be achieved after a post cure cycle of 1 hour at 120°C.
As a casting resin and potting compound, MAX GPE A/B MEDIUM SET demonstrates good dimensional stability excellent electrical insinuative performance and low coefficient of expansion and contraction. General mechanical properties are enhanced after a post cure cycle of 1 hour at 120°C.
MAX GPE A/B Properties
Basic Epoxy Mixing Instructions
Gel Coat Repair
Pre-Mix and Mixing Notes
MAX GPE Application Techniques
Customer Cabin Cruiser Boat Reconstruction Video
Cold Weather Notice